The effect of the surface quality of MgO (1 1 1) substrates seeded by a 3 nm thick Pt layer on the intralayer and interlayer structure of Co/Pt (1 1 1) superlattices was investigated. The superlattices were grown by DC magnetron sputtering. Pre-growth processing of the MgO shows that intensive polishing using a specific H2O/SiO2 suspension prior to growth is mandatory for obtaining long-range structural coherence in the films. The comparison between superlattices grown on re-polished and as-s...The effect of the surface quality of MgO (1 1 1) substrates seeded by a 3 nm thick Pt layer on the intralayer and interlayer structure of Co/Pt (1 1 1) superlattices was investigated. The superlattices were grown by DC magnetron sputtering. Pre-growth processing of the MgO shows that intensive polishing using a specific H2O/SiO2 suspension prior to growth is mandatory for obtaining long-range structural coherence in the films. The comparison between superlattices grown on re-polished and as-supplied substrates shows that the substrate treatment enhances the crystalline in-plane orientation and suppresses abc/acb twin formation. Magnetization measurements were performed using the magneto-optical Kerr effect. Smaller Kerr rotation and lower coercive fields were observed in the highly ordered samples. » weiterlesen» einklappen

Autoren

Klassifikation

DFG Fachgebiet:
Physik der kondensierten Materie

DDC Sachgruppe:
Physik