Pinning and irreversibility behavior in Au-irradiated Bi-2212 films
Physica C. Bd. 235/240. H. 4. 1994 S. 2739 - 2740
Erscheinungsjahr: 1994
ISBN/ISSN: 0921-4534
Publikationstyp: Zeitschriftenaufsatz
Sprache: Englisch
Doi/URN: 10.1016/0921-4534(94)92590-9
| Geprüft | Bibliothek |
Inhaltszusammenfassung
Pinning and irreversibility behavior of dc-sputtered and Au-irradiated Bi-2212 films have been investigated by means of SQUID-magnetometry. For different field regimes a basically different course of the irreversibility line as a result of Au-irradiation is found. A maximum shift of the irreversibility line by 20K occurs at H = 15kOe as a result of irradiation by a dose of ? = 1011cm?1, whereas for higher fields, the efficiency of the columnar defects is reduced. Above H = 15kOe a change in t...Pinning and irreversibility behavior of dc-sputtered and Au-irradiated Bi-2212 films have been investigated by means of SQUID-magnetometry. For different field regimes a basically different course of the irreversibility line as a result of Au-irradiation is found. A maximum shift of the irreversibility line by 20K occurs at H = 15kOe as a result of irradiation by a dose of ? = 1011cm?1, whereas for higher fields, the efficiency of the columnar defects is reduced. Above H = 15kOe a change in the temperature dependence of the irreversibility field occurs indicating a transition from a 3D vortex glass to a 2D vortex lattice. » weiterlesen» einklappen
Autoren
Klassifikation
DFG Fachgebiet:
Physik der kondensierten Materie
DDC Sachgruppe:
Physik